17 4 Ph Stainless Steel Yield Strength

This grade can be easily formed in the austenitic condition similar to type 301 stainless steel and hardened to high strength levels using relatively low heat.

17 4 ph stainless steel yield strength.

For applications requiring high strength and hardness plus corrosion resistance this alloy is an outstanding choice. 17 4 ph stainless steel uns s17400 shaped flat square round fine wire plated and bare wire astm a564 astm 693 ams 5523 ams 5604 ams 5643 17 4ph alloy description 17 4 ph is a martensitic chromium nickel copper precipitation hardening stainless steel that provides an. High strength 17 4 ph stainless steel with a higher chromium content than 15 5 ph stainless steel this high strength 17 4 ph offers better corrosion resistance. 17 4 ph stainless steel is a martensitic precipitation hardening stainless steel that provides an outstanding combination of high strength good corrosion resistance good mechanical properties at temperatures up to 600 f 316 c good toughness in both base metal and welds and short time low temperature heat treatments that minimize warpage and scaling.

17 4 ph steel contains 4 copper and may be hardened by a single low temperature precipitation hardening heat treatment producing excellent mechanical properties at a high strength level. Tensile strength 115 234 σb mpa yield strength 23 σ 0 2 mpa elongation 65 δ5 ψ ψ akv akv j hbs 123 321 hrc 30 17 4ph mechanical properties. It is one of the most widely used precipitation hardening grades as it has high strength hardness up to about 572 f while demonstrating good corrosion resistance in all. In addition it is more cost effective than many high nickel non ferrous alloys.

Tensile strength 231 231 σb mpa yield strength 154 σ 0 2 mpa elongation 56 δ5 ψ ψ akv akv j hbs 235 268 hrc 30. 17 4 ph provides this high strength in combination with good mechanical properties at temperatures of up to 600 f 316 c. 17 4 provides an outstanding combination of high strength good mechanical properties at temperatures up to 600 f 316 c and short duration low temperature heat treatments that minimize warpage and scaling. Type 17 4 is the most common grade of martensitic precipitation hardenable ph alloys.

17 4 stainless steel 17 4 uns s17400. It is also known as 630 stainless steel. Alloy 17 4 is a chromium copper precipitation hardening stainless steel that is used for applications requiring high strength and a moderate level of corrosion resistance.